Name
Property
Applications
More Info
OE5118I
Density
940 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
0,7 g/10min
Vinyl Acetate content by weight
18 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5118I is a copolymer of
ethylene and vinyl acetate
containing 18% vinyl acetate
by weight. Contains BHT as
thermal antioxidant.
Processing Techniques
OE5118I copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5309
Density
935 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
2 g/10min
Vinyl Acetate content by weight
9 %
Applications
Automotive, construction,
pipe and wire and cable products.
HF955MO is a very stiff
polypropylene
homopolymer. This grade
combines unique Borstar
reactor design with Borealis
Nucleation Technology
(BNT) to produce highly-
crystalline polypropylene.
Special Features
Good stiffness
Good impact strength
Improved gloss and
excellent transparency
Excellent organoleptic
properties
OE5325I
Density
948 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
2 g/10min
Vinyl Acetate content by weight
25 %
Applications
Industrial applications
Automotive, construction, pipe
and wire and cable products.
OE5325I is a copolymer of
ethylene and vinyl acetate
containing 25% vinyl
acetate by weight. OE5325I
contains BHT as thermal
antioxidant.
Processing Techniques
OE5325I copolymer shows
excellent thermal stability,
which allows higher
processing temperatures,
if needed. Additional
stabilization could be
required for longer
exposure times.
OE5312I
Density
933 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
2,5 g/10min
Vinyl Acetate content by weight
12 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5312I is a copolymer of
ethylene and vinyl acetate
containing 12% vinyl acetate
by weight. OE5312I contains
BHT as thermal antioxidant.
Processing Techniques
OE5312I copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5315I
Density
937 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
2,5 g/10min
Vinyl Acetate content by weight
15 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5315I is intended for use
in industrial applications and
is sold only for use in
automotive, construction,
pipe and wire and cable
products.
Processing Techniques
OE5315I copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5318I
Density
939 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
2,5 g/10min
Vinyl Acetate content by weight
18 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5318I is a copolymer of
ethylene and vinyl acetate
containing 18% vinyl acetate
by weight. OE5318I contains
BHT as thermal antioxidant.
Processing Techniques
OE5318I copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5328I
Density
950 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
3 g/10min
Vinyl Acetate content by weight
28 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5328I is a copolymer of
ethylene and vinyl acetate
containing 28% vinyl
acetate by weight. OE5328I
contains BHT as thermal
antioxidant.
Processing Techniques
OE5328I in hot melt
adhesive applications is
normally exposed to high
temperatures for long
times. Additional
stabilization could be
required for longer
exposure times.
OE5528I
Density
951 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
6 g/10min
Vinyl Acetate content by weight
28 %
Applications
Automotive, construction,
pipe and wire and cable products.
OE5528I is a copolymer of
ethylene and vinyl acetate
containing 28% vinyl acetate
by weight. OE5528I contains
BHT as thermal antioxidant.
Processing Techniques
OE5528I in hot melt
adhesive applications is
normally exposed to high
temperatures for long
times. Additional
stabilization could be
required for longer
exposure times.
OE5515
Density
935 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
8 g/10min
Vinyl Acetate content by weight
15 %
Applications
Automotive, construction,
pipe and wire and cable products.
OE5515 is a copolymer of
ethylene and vinyl acetate
containing 15% vinyl acetate
by weight. OE5515 contains
BHT as thermal antioxidant.
Processing Techniques
OE5515 copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5518
Density
939 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
8 g/10min
Vinyl Acetate content by weight
18 %
Applications
Industrial applications
Automotive, construction,
pipe and wire and cable products.
OE5518 is a copolymer of
ethylene and vinyl acetate
containing 18% vinyl acetate
by weight. OE5518 contains
BHT as thermal antioxidant.
Processing Techniques
OE5518 copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5828
Density
949 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
25 g/10min
Vinyl Acetate content by weight
28 %
Applications
Automotive, construction,
pipe and wire and cable products.
OE5828 is a copolymer of
ethylene and vinyl acetate
containing 28% vinyl acetate
by weight. OE5828 contains
BHT as thermal antioxidant.
Processing Techniques
OE5828 copolymer shows
excellent thermal stability,
which allows higher
processing temperatures, if
needed. Additional
stabilization could be
required for longer
exposure times.
OE5928
Density
951 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
43 g/10min
Vinyl Acetate content
28 %
Applications
Hot melt adhesives
automotive, construction, pipe
and wire and cable products
OE5928 is a copolymer of
ethylene and vinyl acetate
containing 28% vinyl acetate
by weight.
OE5928 contains BHT as
thermal antioxidant.
Processing Techniques
OE5928 in hot melt
adhesive applications is
normally exposed to high
temperatures for long
times.
OE5918-02
Density
935 kg/m³
Melt Flow Rate (190 °C/2,16 kg)
150 g/10min
Vinyl Acetate content
18 %
Applications
Polymer component in
packaging, pipe, construction,
automotive and wire & cable
products.
OE5918-02 is a copolymer of
ethylene and vinyl acetate
containing 18% vinyl
acetate by weight.
OE5918-02 contains BHT
as thermal antioxidant.
Processing Techniques
OE5918-02 copolymer
shows excellent thermal
stability, which allows
higher processing
temperatures, if needed.
Additional stabilization
could be required for longer
exposure times.