Borealis PP high-flow solutions (PPHP, PPCP, PPRCP). Flow enhancers for production of masterbatch compounding and composites.
– Highly-filled performance masterbatches with over 60% filler content
– Masterbatch systems genuinely compatible with melt blown applications
– Masterbatch systems with improved flow can broaden the window for injection moulding:
– Enabling longer flow path injection lower machine tonnage
– Decreasing pressure in mould and machine longer mould lifespan
– Enabling lower injection temperature means energy reduction, with resulting CO2 reduction and increased sustainability
– Carrier resins enabling improved wet-ability for better dispersion of fillers
Name
Property
Applications
More Info
HF420FB
Homopolymer
Melt Flow Rate (230 °C/2,16 kg)
19 g/10min
Melting temperature (DSC)
161 °C
Molecular weight distribution
Very narrow
Applications
Staple fibre
Continuous filaments
Spunbonded nonwovens
HF420FB is a
polypropylene
homopolymer intended for
fibre applications.
Special Features
Controlled rheology
High flow
Easy processability
Improved melt stability
Optimal product consistency
Optimal resin purity
Good long term heat stability
HH450FB
Homopolymer
Melt Flow Rate (230 °C/2,16 kg)
37 g/10min
Melting temperature (DSC)
161 °C
Molecular weight distribution
Very narrow
Applications
Spunbonded nonwovens
HH450FB is a polypropylene
homopolymer intended for
fibre applications.
Special Features
Very high flow
Controlled rheology
Easy processability
Anti-gasfading stabilisation
Optimised neutral colour
appearance
Optimal resin purity
Optimal product consistency
HJ325MO
Homopolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
50 g/10min
Flexural Modulus
1.500 MPa
Applications
Thin wall containers
Square containers
Caps and closures
HJ325MO is a
polypropylene
homopolymer intended for
injection moulding. Its very
high melt flow makes it
especially suitable for thin-
wall packaging and
products with long flow
length. is designed for high-
speed injection moulding
and contains nucleating and
antistatic additives. The
additives are optimized to
provide reduced tendency
for mould plate-out.
Special Features
Good stiffness
Good impact strength
Excellent antistatic
properties
Improved gloss and
excellent transparency
HC001A-B1
Homopolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
2,7 g/10min
Melting temperature
160 °C
Applications
Carrier for masterbatch and
compounding applications
HC001A-B1 is a
polypropylene
homopolymer grade
typically used in various
masterbatch systems. A
consistant and narrow
particle size distribution
allows a high acceptance of
fillers/pigments during
extrusion and/or grafting
process.
Special Features
Cleanliness
100% Chlorine free
Very low gel level
Very high purity
Narrow particle size
distribution 150 – 425μm
BC250MO
Heterophasic Copolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
4 g/10min
Flexural Modulus
1.100 MPa
Applications
Crates and boxes
Pallets
Technical parts
Bottle trays
Luggage
Containers
BC250MO is a very high
impact polypropylene
heterophasic copolymer
intended for injection
moulding. This grade is
characterized by
combination of good
stiffness, good creep
resistance and very high
impact strength even at low
temperatures.
Special Features
Very good processability
High melt stability
Good stress crack resistance
Good chemical resistance
Good stiffness
BD310MO
Heterophasic Copolymer
Density
905 kg/m3
Melt Flow Rate (230 °C/2,16 kg)
8 g/10min
Tensile Modulus (1 mm/min)
1.400 MPa
Applications
General packaging
Technical parts
Crates
BD310MO is a
heterophasic copolymer.
This grade is characterized
by an optimum
combination of good impact
strength and very high
stiffness.
Special Features
Good impact strength
High stiffness
Shows excellent antistatic
performance
BH348MO
Heterophasic Copolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
50 g/10min
Flexural Modulus
1.050 MPa
Tensile Modulus (1 mm/min)
1.150 MPa
Applications
Thin wall containers
Ice cream containers
BH348MO is a polypropylene
copolymer characterized by
high impact strength, fast flow
and crystallisation speed.
The material is nucleated
with Borealis Nucleation
Technology (BNT). This
grade contains antistatic
and demoulding additives
which, together with
enhanced nucleation, create
a high potential for cycle
time reduction.
BE961MO
Heterophasic Copolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
12 g/10min
Flexural Modulus
1.250 MPa
Tensile Modulus (1 mm/min)
1.200 MPa
Applications
Crates and boxes
Pails
Luggage
Technical parts
BE961MO is a
heterophasic copolymer.
This grade is characterized
by an optimum
combination of high
stiffness, low creep and very
high impact strength.
Special Features
High stiffness
High impact strength
Low creep performance
Good flow behaviour
BH381MO
Heterophasic Copolymer
Density
905 kg/m³
Melt Flow Rate (230 °C/2,16 kg)
35 g/10min
Flexural Modulus
1.600 MPa
Tensile Modulus (1 mm/min)
1.700 MPa
Applications
Crates and boxes
Pails
Technical parts
Houseware and thin wall packaging
Foam
BH381MO is a heterophasic
copolymer. This product is
characterized by an
optimum combination of
very high stiffness and high
impact strength.
Special Features
High stiffness
High impact strength
Very good flow behaviour
PP1121
Specialities
Melt Flow Rate (230 °C/2,16 kg)
3,5 g/10min
Flexural Modulus
1.250 MPa
Tensile Modulus (50 mm/min)
1.350 MPa
Applications
Extruded goods
PP1121 is a high impact
polypropylene heterophasic
copolymer intended for
extruded goods. This grade
is characterized by
combination of good
stiffness, good creep
resistance and very high
impact strength even at low
temperatures. This grade
features high thermal
stability, very low shrinkage
and very good
processability.
Special Features
Good stiffness
Good impact strength
Good stress crack resistance
Very good processability
High melt stability
Very low post extrusion
shrinkage
RA130E
Random Copolymer
Melt Flow Rate (230 °C/2,16 kg)
0,25 g/10min
Tensile Modulus
850 MPa
Tensile Strain at Yield
13,5 %
Applications
Single & multilayer pipes
RA130E is
a low melt flow rate, natural
in colour, random
polypropylene (PP-R).
Special Features
RA130E is a ready made
material in pellet form for
the production of pipes and
fittings.